| Customization: | Available |
|---|---|
| Material: | Acrylic |
| Kind: | Transparent Plastic Sheet |
|
Still deciding? Get samples of US$ 15/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make on Made-in-China.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
|
Product Name | Cast Acrylic Sheet |
| Thickness | 40-50-60mm, 80-90-100mm,
120-150-200mm, Max 1000mm
|
|
| Size | Custom out or bond into any size
Max 3 x 9 meter in stock
|
|
| Materials | 100% purity Acrylic, Piexglass PMMA | |
| Shape | Flat, L-Shape, U-Shape, Curved, Cylinder | |
| Warranty | 20 years Quality Guarantee
No yellowing outside
|
|
| VST | 103ºC Vicat Softening Temperature | |
| Certificate | Pass CE, SVHC, US-CA65, CPSIA Test | |
| Installation | On-site Waterpr
|
|
PROPERTIES
|
VALUES
|
RULES
|
|
Rockwell Hardness
|
112L
|
ISO 2039-2:1999
|
|
Tensile Modulus
|
3150MPa
|
EN ISO 527:2012
|
|
Tensile Strength
|
80.0MPa
|
EN ISO 527:2012
|
|
Tensile Strain at Break
|
3.2%
|
EN ISO 527-1:2012
|
|
Water Absorption
|
0.20%
|
ISO 62:2008 Method 1
|
|
Total Luminous Transmittance
|
92.5%
|
ISO 13468-1:1996
|
|
Vicat Softening Temperature
|
103ºC
|
ISO 306:2013 Method B50
|
|
Light Ageing Test- UV Exposure
|
Grey scale: 5
|
ISO 4892-3:2016 Cycle 1
|
|
Mean Coefficient of Linear Thermal Expansion
|
72×10-6 K-1
|
ISO 11359-1:2014
|
|
Compressive Stress at Yield
|
129MPa
|
EN ISO 604:2003
|
|
Flexural Strength
|
120MPa
|
ISO 178:2013
|
|
Izod Notched Impact Strength
|
101J/m
|
ASTM D256-10 Method A
|
|
Compressive Yield Strength
|
111MPa
|
ASTM D695-15
|
|
Compressive Modulus
|
3450MPa
|
ASTM D695-15
|
|
Shear Strength
|
59.7MPa
|
ASTM D732-17
|
|
Deflection Temperature under Load
|
100.2ºC
|
ASTM D648-18 Method B
|
|
Modulus Elasticity
|
2810MPa
|
ASTM D695-15
|
|
L*W mm
|
T mm
|
L*W mm
|
T mm
|
L*W mm
|
T mm
|
L*W mm
|
T mm
|
|
1300*2500
|
20-70
|
1650*3150
|
20-100
|
5000*1800
|
30-150
|
8200*3000
|
80-250
|
|
1350*2650
|
20-100
|
3200*2200
|
20-110
|
5500*2100
|
30-150
|
8700*3000
|
80-250
|
|
1450*2700
|
20-100
|
3500*1650
|
20-110
|
6200*3000
|
50-250
|
9150*3000
|
100-250
|
|
1600*2600
|
20-100
|
4250*2750
|
30-110
|
6700*3000
|
50-250
|
8100*3700
|
120-300
|
3D drawings intuitively express the structure and effect of acrylic sheets in the project before completion