| Customization: | Available |
|---|---|
| After-sales Service: | 15 Years |
| Warranty: | 15 Years |
|
Still deciding? Get samples of US$ 100/Piece
Order Sample
|
| Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
|---|
| Payment Methods: |
|
|---|---|
| Support payments in USD |
| Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
|---|
| Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
|---|
Suppliers with verified business licenses
Audited Supplier Audited by an independent third-party inspection agency
| Product Name | Cast Acrylic Sheet |
| Thickness | 40-50-60mm, 80-90-100mm,
120-150-200mm, Max 1000mm
|
| Size | Custom out or bond into any size
Max 3 x 9 meter in stock
|
| Materials | 100% purity Acrylic, Piexglass PMMA |
| Shape | Flat, L-Shape, U-Shape, Curved, Cylinder |
| Warranty | 20 years Quality Guarantee
No yellowing outside
|
| VST | 103ºC Vicat Softening Temperature |
| Certificate | Pass CE, SVHC, US-CA65, CPSIA Test |
| Installation | On-site Waterproog and installation Guidance and Service |
Feature 1 :A Grade Cast Acrylic Sheet, SGS conducts factory inspections on more than 20 properties of acrylic sheets
| PROPERTIES | VALUES | RULES |
| Rockwell Hardness | 112L | ISO 2039-2:1999 |
| Tensile Modulus | 3150MPa | EN ISO 527:2012 |
| Tensile Strength | 80.0MPa | EN ISO 527:2012 |
| Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
| Water Absorption | 0.20% | ISO 62:2008 Method 1 |
| Total Luminous Transmittance | 92.5% | ISO 13468-1:1996 |
| Vicat Softening Temperature | 103ºC | ISO 306:2013 Method B50 |
| Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
| Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
| Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
| Flexural Strength | 120MPa | ISO 178:2013 |
| Izod Notched Impact Strength | 101J/m | ASTM D256-10 Method A |
| Compressive Yield Strength | 111MPa | ASTM D695-15 |
| Compressive Modulus | 3450MPa | ASTM D695-15 |
| Shear Strength | 59.7MPa | ASTM D732-17 |
| Deflection Temperature under Load | 100.2ºC | ASTM D648-18 Method B |
| Modulus Elasticity | 2810MPa | ASTM D695-15 |
| L*W mm | T mm | L*W mm | T mm | L*W mm | T mm | L*W mm | T mm |
| 1300*2500 | 20-70 | 1650*3150 | 20-100 | 5000*1800 | 30-150 | 8200*3000 | 80-250 |
| 1350*2650 | 20-100 | 3200*2200 | 20-110 | 5500*2100 | 30-150 | 8700*3000 | 80-250 |
| 1450*2700 | 20-100 | 3500*1650 | 20-110 | 6200*3000 | 50-250 | 9150*3000 | 100-250 |
| 1600*2600 | 20-100 | 4250*2750 | 30-110 | 6700*3000 | 50-250 | 8100*3700 | 120-300 |