Customization: | Available |
---|---|
Material: | Acrylic |
Thickness: | 1.8mm-300mm |
Still deciding? Get samples of US$ 15/Piece
Order Sample
|
Shipping Cost: | Contact the supplier about freight and estimated delivery time. |
---|
Payment methods: | |
---|---|
Support payment in USD |
Secure payments: | Every payment you make at Made-in-china.com is protected by the platform. |
---|
Refund policy: | Claim a refund if your order doesn't ship, is missing, or arrives with product issues. |
---|
Suppliers with verified business licenses
Audited by an independent third-party inspection agency
Material | Lucite Acrylic |
Thickness | 20-300mm customized |
Color | Clear/transparent |
Shape | Customer's Demand |
Surface | High Surface Hardness |
Light transmission | High light transmission(95%) |
Diaphaneity | More than 93% |
Packing | PE film masking on both sides,KT board and angle iron. |
Application | undersea world, Oceanarium, Zoo, Luxurious hotels, Swimming pools and so on. |
PROPERTIES | VALUES | RULES |
Density | 1.19 g/cm3 | ISO 1183-1:2012 Method A |
Rockwell Hardness | 112L | ISO 2039-2:1999 |
Tensile Modulus | 3150MPa | EN ISO 527:2012 |
Tensile Strength | 80.0MPa | EN ISO 527:2012 |
Tensile Strain at Break | 3.2% | EN ISO 527-1:2012 |
Water Absorption | 0.20% | ISO 62:2008 Method 1 |
Total Luminous Transmittance | 93.4% | ISO 13468-1:1996 |
Vicat Softening Temperature | 105ºC | ISO 306:2013 Method B50 |
Light Ageing Test- UV Exposure | Grey scale: 5 | ISO 4892-3:2016 Cycle 1 |
Mean Coefficient of Linear Thermal Expansion | 72×10-6 K-1 | ISO 11359-1:2014 |
Compressive Stress at Yield | 129MPa | EN ISO 604:2003 |
Flexural Strength | 120MPa | ISO 178:2013 |
Compressive Yield Strength | 111MPa | ASTM D695-15 |
Compressive Modulus | 3450MPa | ASTM D695-15 |
Shear Strength | 59.7MPa | ASTM D732-17 |
Deflection Temperature under Load | 100.2ºC | ASTM D648-18 Method B |
Modulus Elasticity | 2810MPa | ASTM D695-15 |